Linear polystyrene-stabilized PdO nanoparticle-catalyzed Mizoroki-Heck reactions in water.

Linear polystyrene-stabilized PdO nanoparticles (PS-PdONPs) were prepared by thermal decomposition of Pd(OAc)(2) in the presence of polystyrene. X-ray diffraction (XRD) and transmission electron microscopy (TEM) indicated the production of PdO nanoparticles. The loading of palladium was determined by inductively coupled plasma-atomic emission spectroscopy (ICP-AES).

Linear polystyrene-stabilized palladium nanoparticles-catalyzed C-C coupling reaction in water.

Linear polystyrene-stabilized PdO nanoparticles (PS-PdONPs) were prepared in water by thermal decomposition of Pd(OAc)(2) in the presence of polystyrene. The immobilization degree of palladium was dependent on the molecular weight of polystyrene, while the size of the Pd nanoparticles was not. Linear polystyrene-stabilized Pd nanoparticles (PS-PdNPs) were also prepared using NaBH(4) and phenylboronic acid as reductants.

Synthesis and characterization of polypyrrole-palladium nanocomposite-coated latex particles and their use as a catalyst for Suzuki coupling reaction in aqueous media.

Polypyrrole-palladium (PPy-Pd) nanocomposite was deposited in situ from aqueous solution onto micrometer-sized polystyrene (PS) latex particles. The PS seed particles and resulting composite particles were extensively characterized with respect to particle size and size distribution, morphology, surface/bulk chemical compositions, and conductivity. PPy-Pd nanocomposite loading onto the PS seed latex particles was systematically controlled over a wide range (10-60 wt %) by changing the weight ratio of the PS latex and PPy-Pd nanocomposite.

Facile preparation of linear polystyrene-stabilized Pd nanoparticles in water.

Palladium nanoparticles can be readily stabilized onto linear polystyrene by a simple procedure. The resultant polystyrene-stabilized Pd has high catalytic activity for Suzuki-Miyaura cross-coupling reaction in water and can be reused without loss of activity.