Aminolysis of Poly-3-Hydroxybutyrate in N,N-Dimethylformamide and 1,4-Dioxane and Formation of Functionalized Oligomers.

The degradation pattern of bacterial poly-3-hydroxybutyrate (PHB) in dimethylformamide (DMF) and dioxane solutions at 100 °C assisted by ethylenediamine, 1,4-diaminobutane and monoaminoethanol was studied. When diamines were introduced into the PHB solution in DMF in the amount of 1 mol of the reagent to 5 or 10 mol of PHB monomers, a rapid decrease in the molecular weight of the polymer was observed. The initial value of the weight average molecular weight (M) 840 kDa had decreased by 20-30 times within the first 10-20 min of the experiment, followed by its gradual decrease to several thousand Da.

Influence of the Filler Particles' Surface Morphology on the Polyurethane Matrix's Structure Formation in the Composite.

This article presents the surface morphology effect of silicon carbide (SiC) particles on the polyurethane binder's structure formation in a dispersed-filled composite. The difference in the morphology and surface relief of filler particles was ensured by the implementation of plasma chemical modification. As a result of this modification, the filler consisted of core-shell particles characterized by a SiC core and a carbon shell (SiC@C), as well as a carbon shell decorated with silicon nanoparticles (SiC@C/SiNP) or nanos (SiC@C/SiNW).