Free-standing arrays of isolated TiO2 nanotubes through supercritical fluid drying.

A common complication in fabricating arrays of TiO(2) nanotubes is that they agglomerate into tightly packed bundles during the inevitable solvent evaporation step. This problem is particularly acute for template-fabricated TiO(2) nanotubes, as the geometric tunability of this technique enables relatively large inter-pore spacings or, from another perspective, more space for lateral displacement. Our work showed that agglomeration results from the surface tension forces that are present as the ambient solvent is evaporated from the nanotube film.

Fabrication of highly-ordered TiO(2) nanotube arrays and their use in dye-sensitized solar cells.

Highly ordered TiO(2) nanotubes were successfully fabricated using a nanoporous alumina templating method. A modified sol-gel route was used to infiltrate the alumina pores with Ti(OC(3)H(7))(4) which was subsequently converted into TiO(2) nanotubes. The average external diameter, tube lengths, and wall thickness achieved were 295 nm, 6-15 microm, and 21-42 nm, respectively.