Combined Arrhenius-Merz Law Describing Domain Relaxation in Type-II Multiferroics.

Electric fields were applied to multiferroic TbMnO_{3} single crystals to control the chiral domains, and the domain relaxation was studied over 8 decades in time by means of polarized neutron scattering. A surprisingly simple combination of an activation law and the Merz law describes the relaxation times in a wide range of electric field and temperature with just two parameters, an activation-field constant and a characteristic time representing the fastest possible inversion. Over the large part of field and temperature values corresponding to almost 6 orders of magnitude in time, multiferroic domain inversion is thus dominated by a single process, the domain wall motion.

Control of Chiral Magnetism Through Electric Fields in Multiferroic Compounds above the Long-Range Multiferroic Transition.

Polarized neutron scattering experiments reveal that type-II multiferroics allow for controlling the spin chirality by external electric fields even in the absence of long-range multiferroic order. In the two prototype compounds TbMnO_{3} and MnWO_{4}, chiral magnetism associated with soft overdamped electromagnons can be observed above the long-range multiferroic transition temperature T_{MF}, and it is possible to control it through an electric field. While MnWO_{4} exhibits chiral correlations only in a tiny temperature interval above T_{MF}, in TbMnO_{3} chiral magnetism can be observed over several kelvin up to the lock-in transition, which is well separated from T_{MF}.

Control of multiferroic domains by external electric fields in TbMnO₃.

The control of multiferroic domains through external electric fields has been studied by dielectric measurements and by polarized neutron diffraction on single-crystalline TbMnO3. Full hysteresis cycles were recorded by varying an external field of the order of several kV mm(-1) and by recording the chiral magnetic scattering as well as the charge in a sample capacitor. Both methods yield comparable coercive fields that increase upon cooling.