Effect of defects on the intrinsic strength and stiffness of graphene.

It is important from a fundamental standpoint and for practical applications to understand how the mechanical properties of graphene are influenced by defects. Here we report that the two-dimensional elastic modulus of graphene is maintained even at a high density of sp(3)-type defects. Moreover, the breaking strength of defective graphene is only ~14% smaller than its pristine counterpart in the sp(3)-defect regime.

High-strength chemical-vapor-deposited graphene and grain boundaries.

Pristine graphene is the strongest material ever measured. However, large-area graphene films produced by means of chemical vapor deposition (CVD) are polycrystalline and thus contain grain boundaries that can potentially weaken the material. We combined structural characterization by means of transmission electron microscopy with nanoindentation in order to study the mechanical properties of CVD-graphene films with different grain sizes.