Nanoscale chirality generated in zinc(II) orthophosphate clusters: evidence by vibrational circular dichroism.

Layered zinc(II) hydroxides (LZH) intercalating the deprotonated forms of -(-) or -(+)-1,1'-binaphthyl-2,2'-diyl hydrogenphosphate (denoted as - or -BNDHPH, respectively) were prepared from Zn(NO) at pH 5 and 60 °C by the mixing method. The obtained hybrid compounds (denoted as - or -BNDHP/LZH, respectively) were heated from room temperature up to 800 °C under nitrogen atmosphere. According to the thermal gravimetric/differential thermal analysis measurements, hydroxyl groups were dehydrated at 270-400 °C, followed by the decomposition of organic components at 420-600 °C.

Intercalation of collagen and soybean peptides into Zn-Al layered double hydroxide.

In order to develop a new type biocompatible organic/inorganic nanohybrid material, an intercalation of collagen peptides (CP) and soybean peptide (SP) into Zn-Al layered double hydroxide (LDH) by the coprecipitation reaction has been investigated. The peptide/LDH has been characterized by chemical analysis, powder X-ray diffraction (XRD), Raman spectroscopy, thermal gravimetric analysis (TG) and transmission electron microscopy (TEM). According to the XRD patterns and Raman spectra, the solid products were found to contain peptide and to show broad diffraction peaks with LDH structures.