Influence of Quaternary Ammonium Salt Functionalized Chitosan Additive as Sustainable Filler for High-Density Polyethylene Composites.

In this study, an antimicrobial packaging material was successfully developed with blends of high-density polyethylene (HDPE) and chitosan (CS) made by melt processing. In the different HDPE/CS composites, the CS content effect (up to 40%), and the addition of quaternary ammonium salt functionalized chitosan (CS-CTAB) as an additive were evaluated by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric analyses (TG), tensile strength, scanning electron microscopy (SEM) and antimicrobial activity. When analyzing the effect of the additive in the different HDPE/CS composites, it was observed that the compositions with 10 and 20 %wt of chitosan showed better elongation values (~13% and 10%) as well as a higher decomposition temperature at 20% mass loss (T20) varying from (321-332 °C and 302-312 °C), respectively, in relation to the other compositions, regardless of the type of additive used, it acted as an antimicrobial agent, promoting inhibition of microbial growth against the strains gram-positive and gram-negative used in this work, making the different HDPE/CS composites suitable candidates for use in food packaging.

The Impact of the Ionic Cross-Linking Mode on the Physical and In Vitro Dexamethasone Release Properties of Chitosan/Hydroxyapatite Beads.

In this study, the effect of the ionic cross-linking mode on the ability to control physical properties and in vitro release behavior of the dexamethasone (DEX) drug from chitosan (CS) and chitosan/hydroxyapatite (CS/HA) beads was investigated. CS solutions without and with HA and DEX were dripped into two coagulation solutions, prepared with a non-toxic ionic crosslinker (sodium tripolyphosphate, TPP) and distilled water, one at pH = 9.0 and other at pH = 6.