Small-angle neutron scattering (SANS) and neutron spin-echo (NSE) have been used to investigate the temperature-dependent solution behaviour of highly-branched poly(N-isopropylacrylamide) (HB-PNIPAM). SANS experiments have shown that water is a good solvent for both HB-PNIPAM and a linear PNIPAM control at low temperatures where the small angle scattering is described by a single correlation length model. Increasing the temperature leads to a gradual collapse of HB-PNIPAM until above the lower critical solution temperature (LCST), at which point aggregation occurs, forming disperse spherical particles of up to 60 nm in diameter, independent of the degree of branching.
View Article and Find Full Text PDFThe nanoscopic adhesive and frictional behaviour of end-grafted poly[2-(dimethyl amino)ethyl methacrylate] (PDMAEMA) films (brushes) in contact with gold- or PDMAEMA-coated atomic force microscope tips in potassium halide solutions with different concentrations up to 300 mM is a strong function of salt concentration. The conformation of the polymers in the brush layer is sensitive to salt concentration, which leads to large changes in adhesive forces and the contact mechanics at the tip-sample contact, with swollen brushes (which occur at low salt concentrations) yielding large areas of contact and friction-load plots that fit JKR behaviour, while collapsed brushes (which occur at high salt concentrations) yield sliding dominated by ploughing, with conformations in between fitting DMT mechanics. The relative effect of the different anions follows the Hofmeister series, with I collapsing the brushes more than Br and Cl for the same salt concentration.
View Article and Find Full Text PDFThe frictional behaviour of end-grafted poly[2-(dimethyl amino)ethyl methacrylate] films (brushes) has been shown by friction force microscopy to be a strong function of pH in aqueous solution. Data were acquired using bare silicon nitride and gold-coated tips, and gold coated probes that were functionalized by the deposition of self-assembled monolayers. At the extremes of pH (pH = 1, 2, and 12), the friction-load relationship was found to be linear, in agreement with Amontons' law of macroscopic friction.
View Article and Find Full Text PDFA series of NIPAM/4-vinyl benzyl chloride copolymers were substituted with 4(5)-imidazole dithioic acid or N-pyrrole dithioic acid to form multi-functional linear dithioate-functional polymers, which can be used as macromolecular transfer agents in a controlled radical polymerisation (RAFT) process. The presence of imidazole dithioate or N-pyrrole dithioate units along the NIPAM copolymer was determined by (1)H NMR, which showed broad CH-imidazole or CH-N-pyrrole resonances. Subsequent reaction of these multi-branch point polymers to produce graft polymers was achieved by reaction with NIPAM in the presence of AIBN.
View Article and Find Full Text PDF