Effective Infiltration of Gel Polymer Electrolyte into Silicon-Coated Vertically Aligned Carbon Nanofibers as Anodes for Solid-State Lithium-Ion Batteries.

This study demonstrates the full infiltration of gel polymer electrolyte into silicon-coated vertically aligned carbon nanofibers (Si-VACNFs), a high-capacity 3D nanostructured anode, and the electrochemical characterization of its properties as an effective electrolyte/separator for future all-solid-state lithium-ion batteries. Two fabrication methods have been employed to form a stable interface between the gel polymer electrolyte and the Si-VACNF anode. In the first method, the drop-casted gel polymer electrolyte is able to fully infiltrate into the open space between the vertically aligned core-shell nanofibers and encapsulate/stabilize each individual nanofiber in the polymer matrix.

Higher-power supercapacitor electrodes based on mesoporous manganese oxide coating on vertically aligned carbon nanofibers.

A study on the development of high-power supercapacitor materials based on formation of thick mesoporous MnO2 shells on a highly conductive 3D template using vertically aligned carbon nanofibers (VACNFs). Coaxial manganese shells of 100 to 600 nm nominal thicknesses are sputter-coated on VACNFs and then electrochemically oxidized into rose-petal-like mesoporous MnO2 structure. Such a 3D MnO2/VACNF hybrid architecture provides enhanced ion diffusion throughout the whole MnO2 shell and yields excellent current collection capability through the VACNF electrode.

Preparation and characterization of TiO2 barrier layers for dye-sensitized solar cells.

A TiO2 barrier layer is critical in enhancing the performance of dye-sensitized solar cells (DSSCs). Two methods to prepare the TiO2 barrier layer on fluorine-doped tin dioxide (FTO) surface were systematically studied in order to minimize electron-hole recombination and electron backflow during photovoltaic processes of DSSCs. The film structure and materials properties were correlated with the photovoltaic characteristics and electrochemical properties.

Tin dioxide@carbon core-shell nanoarchitectures anchored on wrinkled graphene for ultrafast and stable lithium storage.

The SnO2@C@GS composites as a new type of 3D nanoarchitecture have been successfully synthesized by a facile hydrothermal process followed by a sintering strategy. Such a 3D nanoarchitecture is made up of SnO2@C core-shell nanospheres and nanochains anchored on wrinkled graphene sheets (GSs). Transmission electron microscopy shows that these core-shell nanoparticles consist of 3-9 nm diameter secondary SnO2 nanoparticles embedded in about 50 nm diameter primary carbon nanospheres.

Atomic layer deposition of Al-doped ZnO/Al2O3 double layers on vertically aligned carbon nanofiber arrays.

High-aspect-ratio, vertically aligned carbon nanofibers (VACNFs) were conformally coated with aluminum oxide (Al2O3) and aluminum-doped zinc oxide (AZO) using atomic layer deposition (ALD) in order to produce a three-dimensional array of metal-insulator-metal core-shell nanostructures. Prefunctionalization before ALD, as required for initiating covalent bonding on a carbon nanotube surface, was eliminated on VACNFs due to the graphitic edges along the surface of each CNF. The graphitic edges provided ideal nucleation sites under sequential exposures of H2O and trimethylaluminum to form an Al2O3 coating up to 20 nm in thickness.