Attenuation of ultrasound in severely plastically deformed nickel.

Ultrasound attenuation was measured in nickel specimens of about 30 mm diameter prepared using the high pressure torsion technique. The cold working process produced an equivalent shear strain increasing from zero at the center up to 1000% at the edge of the specimen. The fragmentation of the grains due to multiple dislocations led to an ultrafine microstructure with large angle grain boundaries.