Lone-Pair-Enabled Polymorphism and Photostructural Changes in Chalcogenide Glasses.

S- and Se-based chalcogenide glasses are intrinsically metastable and exhibit a number of photo-induced effects unique to this class of materials, reversible photostructural changes and photo-induced anisotropy being major examples. These effects are usually interpreted in terms of the formation of valence alternation pairs and 'wrong' bonds. In this work, using density functional theory simulations, we demonstrate for the case example of As2S3 that a strong decrease in the optical band gap can be achieved if a polymorphic transformation of the local structure from orpiment to that of tetradymite takes place.

Hierarchical Surface Structures and Large-Area Nanoscale Gratings in AsS and AsSe Films Irradiated with Femtosecond Laser Pulses.

Chalcogenide vitreous semiconductors (ChVSs) find application in rewritable optical memory storage and optically switchable infrared photonic devices due to the possibility of fast and reversible phase transitions, as well as high refractive index and transmission in the near- and mid-infrared spectral range. Formed on such materials, laser-induced periodic surface structures (LIPSSs), open wide prospects for increasing information storage capacity and create polarization-sensitive optical elements of infrared photonics. In the present work, a possibility to produce LIPSSs under femtosecond laser irradiation (pulse duration 300 fs, wavelength 515 nm, repetition rate up to 2 kHz, pulse energy ranged 0.

Femtosecond Laser Fabrication of Anisotropic Structures in Phosphorus- and Boron-Doped Amorphous Silicon Films.

Femtosecond laser-modified amorphous silicon (a-Si) films with optical and electrical anisotropy have perspective polarization-sensitive applications in optics, photovoltaics, and sensors. We demonstrate the formation of one-dimensional femtosecond laser-induced periodic surface structures (LIPSS) on the surface of phosphorus- (n-a-Si) and boron-doped (p-a-Si) amorphous silicon films. The LIPSS are orthogonal to the laser polarization, and their period decreases from 1.

Artificial Anisotropy in GeSbTe Thin Films after Femtosecond Laser Irradiation.

GeSbTe (GST225) looks to be a promising material for rewritable memory devices due to its relatively easy processing and high optical and electrophysical contrast for the crystalline and amorphous phases. In the present work, we combined the possibilities of crystallization and anisotropic structures fabrication using femtosecond laser treatment at the 1250 nm wavelength of 200 nm thin amorphous GST225 films on silicon oxide/silicon substrates. A raster treatment mode and photoexcited surface plasmon polariton generation allowed us to produce mutually orthogonal periodic structures, such as scanline tracks (the period is 120 ± 10 μm) and laser-induced gratings (the period is 1100 ± 50 nm), respectively.

Fabricating Femtosecond Laser-Induced Periodic Surface Structures with Electrophysical Anisotropy on Amorphous Silicon.

One-dimensional periodic surface structures were formed by femtosecond laser irradiation of amorphous hydrogenated silicon (a-Si:H) films. The a-Si:H laser processing conditions influence on the periodic relief formation as well as correlation of irradiated surfaces structural properties with their electrophysical properties were investigated. The surface structures with the period of 0.