Mechanistic study of AlO coating effects on lithium deposition and dissolution reaction.

Lithium metal anodes show great promise for use in next-generation secondary batteries, but they suffer from lithium dendrite growth, as well as other issues, which cause safety problems and result in a loss of capacity with time. The use of artificial inorganic solid electrolyte interphase (SEI) layers, such as those comprising AlO, is a promising way to mitigate these disadvantages, but the mechanism behind these observed improvements remains poorly understood. Therefore, in this study, using pulsed laser deposition (PLD), the surface of a Cu electrode was coated with a physicochemically stable and mechanically strong AlO thin film, and the effects of the film coating on the lithium deposition and dissolution behaviour were investigated.

Computational studies on defect chemistry and Li-ion conductivity of spinel-type LiAlO as coating material for Li-metal electrode.

Li-metal rechargeable batteries are an attractive option for devices that require an extremely high specific energy density, high robustness, and long-term durability, such as high-altitude platform stations. However, Li dendrite growth during charge-discharge cycling causes short-circuit problems. One technical solution is to form an intermediate layer between the Li metal and electrolyte.