Joining copper oxide nanotube arrays driven by the nanoscale Kirkendall effect.

Various annealing conditions (environment, temperature, and duration) are applied to study the nanoscale Kirkendall effect of copper (Cu) nanowire (NW) arrays on a Si substrate. The results show that an appropriate amount of oxygen supply is crucial for uniform transformation from Cu NWs (average diameter ∼50 nm) into Cu oxide nanotube arrays. An annealing duration of 30 min at 200 °C in a low vacuum environment reveals that the voids are not uniformly distributed at the Cu/Cu oxide interface.