Development of chitosan oligosaccharide-modified gold nanorods for in vivo targeted delivery and noninvasive imaging by NIR irradiation.

In the present study, we demonstrate the synthesis and applications of multifunctional gold nanorod-based probes for specific targeting and noninvasive imaging based on localized heating generated by gold nanorods after NIR irradiation. The structural design of the probe consists of MUA (11-mercaptoundecanoic acid)-capped gold nanorods covalently linked with low-molecular-weight chitosan oligosaccharide (M(w) ~5000) via carbodiimide (EDC) coupling agent. This surface modification is performed for complete replacement of toxic CTAB (hexadecyltrimethyl-ammonium chloride) and acid-responsive delivery of gold nanorods in acidic environment as known to be present at tumor surrounding areas.

Synthesis of tunable and multifunctional Ni-doped near-infrared QDs for cancer cell targeting and cellular sorting.

Here, we report the facile preparation of tunable magnetic Ni-doped near-infrared (NIR) quantum dots (MNIR-QDs) as an efficient probe for targeting, imaging, and cellular sorting applications. We synthesized the MNIR-QDs via a hot colloidal synthesis approach to yield monodisperse and tunable QDs. These hydrophobic QDs were structurally and compositionally characterized and further functionalized with amino-PEG and carboxyl-PEG to improve their biocompatibility.

Development of lipid targeting Raman probes for in vivo imaging of Caenorhabditis elegans.

A simple, sensitive, and highly specific lipid targeting Raman probe (Nile red coated silver nanoparticles) has been developed to image living nematode Caenorhabditis elegans (C. elegans). Our idea of imaging lipids in C.

Direct synthesis of nanocrystalline silver from the reaction between silver carboxylates and n-trioctylphosphine.

Neat n-Trioctylphosphine (TOP) has been used for the first ever time for reduction of silver nitrate and silver carboxylates (citrate, oleate, and myristate) under mild thermal reaction conditions. UV-visible absorption measurements of re-dispersible silver particles that were obtained by reduction of silver myristrate (product-IV) and silver nitrate (product-I) showed surface plasmon resonance absorption peak at 400 nm. The powder XRD pattern of fcc zero-valent silver resulted in diameters in the range of about 25-30 nm.