[ Analysis of Polyethylene Liner Wear Performance at 3 and 5 Million Cycles].

Objective: The purpose of this study is to compare the wear properties of UHMWPE acetabular liners after undergoing 3 million (3 Mc) and 5 million (5 Mc) cycles of wear testing. The results will serve as a reference for the design of testing for hip prostheses and as a control for clinical revision removals.

Methods: Wear tests were conducted on three different sizes of acetabular liners (28 mm, 32 mm, and 36 mm internal diameters) using a hip simulator to determine the amount of wear after 3 and 5 million cycles.

Wear Analysis of Tibial Inserts Made of Highly Cross-Linked Polyethylene Supplemented with Dodecyl Gallate before and after Accelerated Aging.

The wear of the tibial insert is one of the primary factors leading to the failure of total knee arthroplasty. As materials age, their wear performance often degrades. Supplementing highly cross-linked polyethylene (HXLPE) with dodecyl gallate (DG) can improve the oxidation stability of tibial inserts for use in total knee arthroplasty (TKA).

In Vitro Analysis of Wearing of Hip Joint Prostheses Composed of Different Contact Materials.

Cobalt-chromium-molybdenum alloy (CoCrMo) and ceramic are the two most common materials for the femoral head in hip joint prostheses, and the acetabular liner is typically made from ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE), or highly cross-linked polyethylene blended with Vitamin E (VEXLPE). The selection of suitable materials should consider both wear performance and cost-effectiveness. This study compared the wear rate between different friction pairs using a hip joint simulator and then recommended a suitable prosthesis based on the corresponding processing technology and cost.

Wear Assessment of Tibial Inserts Made of Highly Cross-Linked Polyethylene Supplemented with Dodecyl Gallate in the Total Knee Arthroplasty.

Background: the wear of tibial insert is still one of primary factors leading to failure of total knee arthroplasty (TKA). Dodecyl gallate (DG) has shown improvements in the oxidation stability of highly cross-linked polyethylene (HXLPE). This study aimed to assess the application of HXLPE supplemented with DG (HXLPE-DG) on the tibial insert in TKA concerning the wear resistance and the potential impact on implant fixation; Methods: tibial inserts made of HXLPE-DG were subjected to a 3 million loading-cycle wear test following ISO 14243-1:2009.