Effects of ultrasonic treatment and homogenization on physicochemical properties of okara dietary fibers for 3D printing cookies.

This paper presents a means to modify the attributes of okara fiber using ultrasonic and high-speed shearing treatment. The results of scanning electron microscopy and differential scanning calorimetry reveal that the modified okara fiber demonstrates small particle size and high thermal stability. When the 500 W-15,000 rpm combination is used for okara-fiber treatment, the latter exhibits excellent swelling (SC) as well as water- and oil-holding capacities.

Preparation, characterization, and 3D printing verification of chitosan/halloysite nanotubes/tea polyphenol nanocomposite films.

In this study, chitosan/halloysite nanotubes/tea polyphenol (CS/HNTs/TP) nanocomposite films were prepared by the solution casting method. The scanning electron microscopy (SEM) result showed that the nanocomposite film with a CS/HNTs ratio of 6:4 and a TP content of 10% (C6H4-TP10) had a relatively smooth surface and a dense internal structure. The water vapor barrier property of the nanocomposite film was improved due to the tortuous channels formed by the HNTs.