Nitrogen-doped hollow carbon spheres with tunable shell thickness for high-performance supercapacitors.

Nitrogen-doped hollow carbon spheres (NHCSs) are well prepared by using CuO microspheres as a hard template and 3-aminophenol formaldehyde resin polymer as carbon and nitrogen precursors. The thickness of the carbon shell can be easily controlled in the range of 15-84 nm by simply adjusting the weight ratios of the precursors to CuO microspheres, and the CuO templates can also be further reused. Physicochemical characterization demonstrates that the obtained NHCSs possess a well-developed hollow spherical structure, thin carbon shell and high nitrogen doping content.

Three-dimensional low symmetry mesoporous silica structures templated from tetra-headgroup rigid bolaform quaternary ammonium surfactant.

Two kinds of highly ordered mesoporous silica materials (FDU-11, FDU-13) with novel three-dimensional (3-D) tetragonal and orthorhombic structures were synthesized by using tetra-headgroup rigid bolaform quaternary ammonium surfactant [(CH(3))(3)NCH(2)CH(2)CH(2)N(CH(3))(2)CH(2)(CH(2))(11)OC(6)H(4)C(6)H(4)O(CH(2))(11)CH(2)N(CH(3))(2)CH(2)CH(2)CH(2)N(CH(3))(3).4Br] (C(3-12-12)(-)(3)) as a template under alkaline conditions. High-resolution transmission electron microscopy (HRTEM), small-angle X-ray scattering (SAXS), and X-ray diffraction (XRD) show that mesoporous silica FDU-11 has primitive tetragonal P4/mmm structure with cell parameters a = b = 8.

A novel ordered cubic mesoporous silica templated with tri-head group quaternary ammonium surfactant.

An ordered mesoporous silica with novel cubic structure (space group Fd3m) has been synthesized by using tri-head group quaternary ammonium surfactants [CmH2m + 1N+(CH3)2CH2CH2N+(CH3)2CH2CH2CH2N+(-)(CH3)(3).3Br-] (Cm-2-3-1, m = 14, 16, 18) as the structure-directing agents under basic conditions at low temperature.