Luminescence properties of a new green afterglow phosphor NaBaScSi2O7:Eu(2+).

A novel green afterglow phosphor NaBaScSi2O7:Eu(2+) was prepared by a solid state reaction under a reductive atmosphere. The NaBaScSi2O7:Eu(2+) phosphor shows two emission bands centered at about 424 (weak) and 502 nm (strong) due to the substitution of Eu(2+) in both Ba(+) and Na(2+) sites, and energy transfer from EuBa (424 nm) to EuNa (502 nm) was found. Both EuBa and EuNa contribute to the afterglow process while EuNa dominates.