Formation of highly graphitic char derived from phenolic resin carbonization by Ni-Zn-B alloy.

The formation of highly graphitic phenolic resin chars (GPFCs) during catalytic carbonization at relatively low reaction temperature (1200-1600 °C) using novel Ni-Zn-B alloy catalyst with small amount of addition (5-15%) was systematically studied. Only two kinds of graphites (turbostratic graphite and ordered graphite) can be found in GPFCs after catalytic carbonization with Ni-Zn-B and their proportions were changed with reaction conditions. When Ni-Zn-B was involved at 1200-1600 °C, the phenolic resin char was fully transformed to be graphite, and ordered graphite content increased to 28.