Surface stiffening and enhanced photoluminescence of ion implanted cellulose - polyvinyl alcohol - silica composite.

Novel Cellulose (Cel) reinforced polyvinyl alcohol (PVA)-Silica (Si) composite which has good stability and in vitro degradation was prepared by lyophilization technique and implanted using N(3+) ions of energy 24keV in the fluences of 1×10(15), 5×10(15) and 1×10(16)ions/cm(2). SEM analysis revealed the formation of microstructures, and improved the surface roughness on ion implantation. In addition to these structural changes, the implantation significantly modified the luminescent, thermal and mechanical properties of the samples.

Silver ion impregnated composite biomaterial optimally prepared using zeta potential measurements.

Biodegradable, antimicrobial composite of various silver ion concentrations was synthesized using zeta potential and isoelectric point measurements, for a controlled release of silver ions, and in addition to assess the effect of protein adsorption with the increase of the silver ion concentration. The interaction between hydroxyapatite (HAp) and silver incorporated hydroxyapatite (AgHAp) with gelatin was increased by optimally adjusting the zeta potential and isoelectric point of the ceramic (HAp and AgHAp), and bio-polymer individually. The electrostatic interactions between the ceramic and biopolymer were confirmed, through shifts in N-H stretching, decrease in the swelling ratio, and increase in the degradation temperature observed by the derivative thermo-gravimetric analysis (DTG).

Freeze dried cross linking free biodegradable composites with microstructures for tissue engineering and drug delivery application.

Biodegradable laminated polymer composites of agarose (A), gelatin (G) and hydroxyapatite (HAp) having 3D network of interconnected pores (1-500 μm) were fabricated without using cross linking agents. The incorporation of HAp to A, G and AG had considerable influence on the swelling behaviour, drug release and haemolytic activity. A-HAp scaffolds demonstrated interconnected porosity with extended drug release.