White emission from non-planar InGaN/GaN MQW LEDs grown on GaN template with truncated hexagonal pyramids.

Non-planar InGaN/GaN multiple quantum well (MQW) structures are grown on a GaN template with truncated hexagonal pyramids (THPs) featuring c-plane and r-plane surfaces. The THP array is formed by the regrowth of the GaN layer on a selective-area Si-implanted GaN template. Transmission electron microscopy shows that the InGaN/GaN epitaxial layers regrown on the THPs exhibit different growth rates and indium compositions of the InGaN layer between the c-plane and r-plane surfaces.

Dual-wavelength GaN-based LEDs grown on truncated hexagonal pyramids formed by selective-area regrowth on Si-implanted GaN templates.

GaN-based blue light-emitting diodes (LEDs) with micro truncated hexagonal pyramid (THP) array were grown on selective-area Si-implanted GaN (SIG) templates. The GaN epitaxial layer regrown on the SIG templates exhibited selective growth and subsequent lateral growth to form the THP array. The observed selective-area growth was attributed to the different crystal structures between the Si-implanted and implantation-free regions.

Vertical InGaN light-emitting diodes with a sapphire-face-up structure.

Vertical GaN-based light-emitting diodes (LEDs) were fabricated with a Si substrate using the wafer-bonding technique. Lapping and dry-etching processes were performed for thinning the sapphire substrate instead of removing this substrate using the laser lift-off technique and the thinning process associated with the wafer-bonding technique to feature LEDs with a sapphire-face-up structure and vertical conduction property. Compared with conventional lateral GaN/sapphire-based LEDs, GaN/Si-based vertical LEDs exhibit higher light output power and less power degradation at a high driving current, which could be attributed to the fact that vertical LEDs behave in a manner similar to flip-chip GaN/sapphire LEDs with excellent heat conduction.

Linear photon up-conversion of 450 meV in InGaN/GaN multiple quantum wells via Mn-doped GaN intermediate band photodetection.

Up-converted heterostructures with a Mn-doped GaN intermediate band photodetection layer and an InGaN/GaN multiple quantum well (MQW) luminescence layer grown by metal-organic vapor-phase epitaxy are demonstrated. The up-converters exhibit a significant up-converted photoluminescence (UPL) signal. Power-dependent UPL and spectral responses indicate that the UPL emission is due to photo-carrier injection from the Mn-doped GaN layer into InGaN/GaN MQWs.

Characteristics of InGaN-based concentrator solar cells operating under 150X solar concentration.

InGaN/sapphire-based photovoltaic (PV) cells with blue-band GaN/InGaN multiple-quantum-well absorption layers grown on patterned sapphire substrates were characterized under high concentrations up to 150-sun AM1.5G testing conditions. When the concentration ratio increased from 1 to 150 suns, the open-circuit voltage of the PV cells increased from 2.

Enhanced output power of GaN-based LEDs with embedded AlGaN pyramidal shells.

In this article, the characteristics of GaN-based LEDs grown on Ar-implanted GaN templates to form inverted Al0.27Ga0.83N pyramidal shells beneath an active layer were investigated.

InGaN light-emitting diodes with oblique sidewall facets formed by selective growth on SiO₂ patterned GaN film.

In this study, GaN-based light-emitting diodes (LEDs) with naturally formed oblique sidewall facets (OSFs) were fabricated through a selective regrowth process. The SiO₂ mask layer was patterned on a heavily doped n-GaN template layer rather than on a sapphire substrate. As a result, the periphery of the LED included several OSFs around the regrown GaN mesa.