Effect of sulfonation degree on molecular weight, thermal stability, and proton conductivity of poly(arylene ether sulfone)s membrane.

Direct copolymerization of sulfonated and non-sulfonated difluorodiphenyl sulfones as dihalide monomers with hydroquinone and also 4,4'-(4,4'-sulfonylbis-(1,4-phenylene)bis(oxy)) diphenol as diols led to preparation of two series of poly(arylene ether sulfone)s. Copolymers with different degrees of sulfonation (40, 50 and 60%) were synthesized in order to evaluate their potential for fuel cell application. H-NMR, FT-IR, and mass spectroscopy were used for characterization of prepared monomers and copolymers.

Synthesis and characterization of antibacterial polyurethane coatings from quaternary ammonium salts functionalized soybean oil based polyols.

In this study, a simple and versatile synthetic approach was developed to prepare bactericidal polyurethane coatings. For this purpose, introduction of both quaternary ammonium salts (QASs), with well-known antibacterial activity, and reactive hydroxyl groups on to the backbone of soybean oil was considered. Epoxidized soybean oil was reacted with diethylamine and the intermediate tertiary amine containing polyol was reacted with two different alkylating agents, methyl iodide and benzyl chloride, to produce MQAP and BQAP, respectively.

Synthesis and evaluation of antibacterial polyurethane coatings made from soybean oil functionalized with dimethylphenylammonium iodide and hydroxyl groups.

Preparation of antibacterial polyurethane coatings from novel functional soybean oil was considered in this work. First, epoxidized soybean oil (ESBO) as a low price and widely available renewable resource raw material was subjected to the reaction with aniline using an ionic liquid as a green catalyst. The intermediate phenylamine containing polyol (SAP) was then methylated by reaction with methyl iodide to produce a polyol (QAP) with pendant dimethylphenylammonium iodide groups.