Low-energy electron scattering on deuterated nanocrystalline diamond films-a model system for understanding the interplay between density-of-states, excitation mechanisms and surface versus lattice contributions.

Electron energy loss spectrum, elastic reflectivity and selected vibrational excitation functions were measured by High Resolution Electron Energy Loss Spectroscopy (HREELS) for deuterated nanocrystalline dc GD CVD diamond films. The electron elastic reflectivity is strongly enhanced at about 13 eV, as a consequence of the second absolute band gap of diamond preserved up to the surface for D-nano-crystallites. The pure bending modes δ(CD(x)) at 88 meV and 107 meV are dominantly excited through the impact mechanism and their vibration excitation functions mimic the electron elastic reflectivity curve.

Hydrogen bonding configuration and thermal stability of ambient exposed and in situ hydrogenated polycrystalline diamond surfaces studied by high resolution electron energy loss spectroscopy.

In this work we report on an investigation of hydrogen bonding and thermal stability on the surface of poly-crystalline diamond by high resolution electron energy loss spectroscopy (HR-EELS). Diamond films were grown on silicon substrates from CH(4)/H(2) as well as from CD(4)/D(2) gas mixtures by hot filament chemical vapor deposition (HF-CVD). The impact of ex situ ambient exposure on hydrogen bonding and its thermal stability was examined for: (i) as deposited films from a CH(4)/H(2) gas mixture; (ii) the same sample treated ex situ in micro-wave activated hydrogen plasma; and (iii) as deposited films from a CD(4)/D(2) gas mixture.