8.01% CuInGaSe2 solar cells fabricated by air-stable low-cost inks.

CuInGaSe(2) (CIGS), a promising thin film solar cell material, has gained lots of attention in decades due to its high energy conversion efficiency and potential lower manufacture cost over conventional Si solar cells. As a cheaper processing method compared to vacuum-based techniques, solution-based deposition has been successfully applied to fabricate electronic devices, such as transistors and solar cells. In this paper, we reported CIGS thin film solar cells with an energy conversion efficiency reaching up to 8.

Low-temperature, high-performance, solution-processed indium oxide thin-film transistors.

Solution-processed In(2)O(3) thin-film transistors (TFTs) were fabricated by a spin-coating process using a metal halide precursor, InCl(3), dissolved in acetonitrile. A thin and uniform film can be controlled and formed by adding ethylene glycol. The synthesized In(2)O(3) thin films were annealed at various temperatures ranging from 200 to 600 °C in air or in an O(2)/O(3) atmospheric environment.