New route for self-assembly of α-lactalbumin nanotubes and their use as templates to grow silver nanotubes.

Nanotubes are formed by self-assembly of α-lactalbumin milk protein following a different route than established for the hydrolysis which involves V8 enzyme, phosphate buffer and appropriate amounts of calcium at neutral pH. The resulting nanotubes are used as templates for the growth of conductive silver nanotubes. TEM, SEM-EDS, AFM and FTIR are used for characterization.

Direct measurement of interaction forces between bovine serum albumin and poly(ethylene oxide) in water and electrolyte solutions.

The net interaction between a probe tip coated with bovine serum albumin (BSA) protein and a flat substrate coated with poly(ethylene oxide) (PEO) polymer was measured directly on approach in water and electrolyte solutions using AFM. The approach force curve between the two surfaces was monotonically repulsive in water and in electrolyte solutions. At pH ~5, slightly above the isoelectric point (pI) of BSA, and at large distances, the force was dominated by electrostatic repulsion between the oxygen atoms of the incoming protein with those belonging to the ether groups of PEO.

Nanoscale adhesive forces between silica surfaces in aqueous solutions.

Nanoscale adhesive forces between a colloidal silica probe and a flat silica substrate were measured with an atomic force microscope (AFM) in a range of aqueous NaCl, CaCl2, and AlCl3 solutions, with concentrations ranging from 10(-)(6) to 10(-)(2) M at pH ∼5.1. Notably, the measured force curves reveal large pull-off forces in water which increase in electrolyte solutions, with jump-off-contact occurring as a gradual detachment of the probe from the flat substrate rather than as a sharp discontinuous jump.

AFM forces between mica and polystyrene surfaces in aqueous electrolyte solutions with and without gas bubbles.

Force curves between a flat mica substrate and a polystyrene microsphere were measured with an atomic force microscope (AFM) in carefully degassed water and aqueous NaCl, CaCl2, and AlCl3 solutions. The pH of the water used does not change significantly with degassing treatment, and its value remains close to 6. Electrolyte concentration ranges from 10-4 to 10-2M and pH from 4.

Nanoscale repulsive forces between mica and silica surfaces in aqueous solutions.

Nanoscale repulsive forces between mineral surfaces in aqueous solutions were measured for the asymmetric mica-silica system. The force measured with an atomic force microscope (AFM) has universal character in the short range, less than ∼1 nm or about 3-4 water molecules, independent of solution conditions, that is, electrolyte ion (Na, Ca, Al), concentration (10(-6)-10(-2)M), and pH (3.9-8.

Short-range forces between glass surfaces in aqueous solutions.

We found that the force between glass surfaces measured with an atomic force microscope (AFM) has universal character in the short range, less than approximately 1 nm or about 3-4 water molecules, independent of solution conditions, that is, electrolyte ion size, charge and concentration and pH. Our results suggest that the excess DLVO force, obtained by subtracting the DLVO theory with a charge regulation model from the AFM force data, essentially does not change with the electrolytes Na, Ca, and Al, in the range of concentration from 10(-6) to 10(-2) M and the range of pH from 3.1 to 7.