Soluble Fluorinated Cardo Copolyimide as an Effective Additive to Photopolymerizable Compositions Based on Di(meth)acrylates: Application for Highly Thermostable Primary Protective Coating of Silica Optical Fiber.

The development of photocurable compositions is in high demand for the manufacture of functional materials for electronics, optics, medicine, energy, etc. The properties of the final photo-cured material are primarily determined by the initial mixture, which needs to be tuned for each application. In this study we propose to use simple systems based on di(meth)acrylate, polyimide and photoinitiator for the preparation of new photo-curable compositions.

Spectrum collapse in a 7-core Yb-doped fiber laser with an array of fs-inscribed fiber Bragg gratings.

Femtosecond inscription of fiber Bragg gratings (FBGs) in each core of a cladding-pumped seven-core Yb-doped fiber enables efficient (≈70%) 1064-nm lasing in a robust all-fiber scheme with ≈33 W power, nearly the same for uncoupled and coupled cores. However, the output spectrum is quite different: without coupling, seven individual lines corresponding to the in-core FBG reflection spectra sum up into a broad (0.22 nm) total spectrum, whereas the multiline spectrum collapses into a single narrow line at strong coupling.

Advanced distributed feedback lasers based on composite fiber heavily doped with erbium ions.

Specially designed composite heavily Er-doped fiber in combination with unique point-by-point inscription technology by femtosecond pulses at 1,026 nm enables formation of distributed-feedback (DFB) laser with ultra-short cavity length of 5.3 mm whose parameters are comparable and even better than those for conventional Er-doped fiber DFB lasers having much longer cavity. The composite fiber was fabricated by melting rare-earth doped phosphate glass in silica tube.

Fabrication of Bragg gratings in microstructured and step index Bi-SiO2 optical fibers using an ArF laser.

An ArF excimer laser was used to fabricate Bragg gratings in fibers with Bi-SiO(2) core and microstructured or F-doped claddings without fiber presensitization. Average and modulated refractive index changes of 2.7 × 10(-4) and 1.

Mechanisms of optical losses in Bi:SiO2 glass fibers.

The mechanisms of optical losses in bismuth-doped silica glass (Bi:SiO(2)) and fibers were studied. It was found that in the fibers of this composition the up-conversion processes occur even at bismuth concentrations lower than 0.02 at.

Broadband wavelength conversion in a germanosilicate-core photonic crystal fiber.

A photonic crystal fiber with a germanosilicate core having a nonlinear coefficient of 40 (W km)(-1) near the single dispersion zero at 1.09 microm is fabricated and studied. Broadband parametric wavelength conversion of the Ti:sapphire laser output tunable at 0.