Structural, Mechanical, and Tribological Properties of Oriented Ultra-High Molecular Weight Polyethylene/Graphene Nanoplates/Polyaniline Films.

Preparing high-strength polymeric materials using an orientation drawing process is considered one of the most urgent topics in the modern world. Graphene nanoplates/polyaniline (GNP/PANI) were added to the commercial grade UHMWPE (GUR 4120) matrix as a filler with antifriction properties. The effect of GNP/PANI addition on the structure, the orientation process, the void formation (cavitation), the mechanical, and tribological properties was studied using differential scanning calorimetry (DSC), dynamical mechanical analysis (DMA), and scanning electron microscopy (SEM).

The Analysis of Micro-Scale Deformation and Fracture of Carbonized Elastomer-Based Composites by In Situ SEM.

Carbonized elastomer-based composites (CECs) possess a number of attractive features in terms of thermomechanical and electromechanical performance, durability in aggressive media and facile net-shape formability, but their relatively low ductility and strength limit their suitability for structural engineering applications. Prospective applications such as structural elements of micro-electro-mechanical systems MEMS can be envisaged since smaller principal dimensions reduce the susceptibility of components to residual stress accumulation during carbonization and to brittle fracture in general. We report the results of in situ in-SEM study of microdeformation and fracture behavior of CECs based on nitrile butadiene rubber (NBR) elastomeric matrices filled with carbon and silicon carbide.

Low-Temperature Carbonized Elastomer-Based Composites Filled with Silicon Carbide.

Thermally stable composites obtained by the low-temperature carbonization of an elastomeric matrix filled with hard dispersed silicon carbide particles were obtained and investigated. Evolution of the microstructure and of mechanical and thermal characteristics of composites during thermal degradation and carbonization processes in a wide range of filling from 0 to 450 parts per hundred rubber was studied. For highly filled composites, the compressive strength values were found to be more than 200 MPa; Young's modulus was more than 15 GPa.

The Structural and Mechanical Properties of the UHMWPE Films Mixed with the PE-Wax.

Since obtaining a highly oriented structure based on a large-scale commercial ultra-high molecular weight polyethylene (UHMWPE) is considered very difficult due to its high molecular weight and melting index, modifying the structure of these cheap commercial UHMWPE brands into a supra-molecular structure with fiber-forming properties by adding a small amount of polyethylene wax (PE-wax) will provide the possibility to obtain highly oriented UHMWPE products with enhanced mechanical and tribological properties. In this work, highly oriented UHMWPE/PE-wax films were prepared. The PE-wax affected the UHMWPE as an intermolecular lubricant.

Ultra-High Molecular Weight Polyethylene/Titanium-Hybrid Implant for Bone-Defect Replacement.

A hybrid implant with a structure mimicking that of natural bone was developed. Titanium alloy Ti-6Al-4V prepared with three-dimensional (3D)-printing technology was used to simulate the cortical-bone layer. The mismatch in the mechanical properties of bone and titanium alloy was solved by creating special perforations in the titanium's surface.