Particleboards Bonded by an Imidazole-Based Adhesive System.

Particleboards with different combinations of the adhesive material imidazole, citric acid, and sorbitol were produced. Softwood sawdust from a Swedish sawmill was mixed with an aqueous solution of the chemicals and then dried to 0% moisture content prior to pressing. The boards were pressed to a target density of 700 kg m at either 200 °C or 220 °C for 10 min.

Properties and Emissions of Three-Layer Particleboards Manufactured with Mixtures of Wood Chips and Partially Liquefied Bark.

Partial liquefaction of residual biomass shows good potential for developing new materials suitable for making bio-based composites. Three-layer particleboards were produced by replacing virgin wood particles with partially liquefied bark (PLB) in the core or surface layers. PLB was prepared by the acid-catalyzed liquefaction of industrial bark residues in polyhydric alcohol.

Application of liquefied wood as a new particle board adhesive system.

Different types of southern European hardwoods and softwoods were subjected to a liquefaction process with glycerol/diethylene glycol. The liquefied spruce wood was reacted in a condensation reaction in the hot press with different melamine-formaldehyde and melamine-urea-formaldehyde resin precursors and used as adhesives for wood particle boards. The mechanical properties of these particle boards and the determination of formaldehyde release, proved that addition of 50% of the liquefied wood to such resin precursors caused the product to meet the European standard quality demands for particle boards.