Bond Strength and Adhesion Mechanisms of Novel Bone Adhesives.

Bone adhesives offer distinct advantages over the use of screws to attached internal fixation plates (IFPs). As the chemical composition of bone is similar to dentine, it is possible that the types of monomers used to make dentine adhesives could be utilised to affix IFPs to bone. The ability to attach a bio-resorbable IFP to porcine bone was assessed for the monomer 10-methacryloyloxydecyl dihydrogen phosphate (MDP), used either as a homopolymer or a copolymer with urethane dimethacrylate (MDP + U).

Centrifugally spun PHBV micro and nanofibres.

This paper reports the first study on centrifugal spinning of PHBV fibres. Fibres were spun from solution using a range of polymer concentrations, spin speeds and spinneret to collector distances. A PHBV polymer concentration of 25% w/v spun at 9000rmin produced the highest quality fibres, with fibre diameters predominantly in the 0.

Development of a methacrylate-terminated PLGA copolymer for potential use in craniomaxillofacial fracture plates.

We synthesised methacrylate-terminated PLGA (HT-PLGA, 85:15 LA:GA, 169kDa), for potential use as an adhesively attached craniomaxillofacial fracture fixation plate. The in vitro degradation of molecular weight, pH and flexural modulus were measured over 6weeks storage in PBS at 37°C, with commercially available high (225kDa, H-PLGA) and low (116kDa, L-PLGA) molecular weight 85:15 PLGAs used as comparators. Molecular weights of the materials reduced over 6weeks, HT-PLGA by 48%, H-PLGA by 23% and L-PLGA by 81%.