Cationic Order-Disorder in Double Scheelite Type Oxides: the Case Study of Fergusonite LaSiMoO.

Up to now, the possible occurrence of a cationic ordering on the tetrahedral sublattices of stoichiometric double scheelite-type oxides was not settled, with somewhat contradictory X-ray diffraction and optical measurements [Blasse, G. . , , 2091].

Investigation of Polyol Process for the Synthesis of Highly Pure BiFeO Ovoid-Like Shape Nanostructured Powders.

Exclusive and unprecedented interest was accorded in this paper to the synthesis of BiFeO nanopowders by the polyol process. The synthesis protocol was explored and adjusted to control the purity and the grain size of the final product. The optimum parameters were carefully established and an average crystallite size of about 40 nm was obtained.

Reduction Kinetics of La2Mo2O9 and Phase Evolution during Reduction and Reoxidation.

An amorphous reduced form of oxide ion conductor La2Mo2O9 had been proposed as sulfur-tolerant anode material for solid oxide fuel cell, but its oxygen content was not known. In this paper, we investigate the reduction kinetics by diluted hydrogen of La2Mo2O9 to amorphous, and the oxygen range of the amorphous form. The reduction kinetics is studied as a function of the powder specific surface area and of the temperature, on powders synthesized by solid state reaction and by polyol process using two different solvents.