Study on the Curing and Foaming of Surfactant-Modified Geopolymer Gels Based on Ash and Slag Waste from Coal Combustion.

This study explores the influence of temperature-time conditions, surfactants, and varied waste compositions on the curing of geopolymer gels, a foam formation with the properties of porous geopolymers. Findings reveal that a 6 h curing period leads to a density of 435 kg/m and strength of 0.66 MPa, with notable improvements at 12 h.

Managing Excess Lead Iodide with Functionalized Oxo-Graphene Nanosheets for Stable Perovskite Solar Cells.

Stability issues could prevent lead halide perovskite solar cells (PSCs) from commercialization despite it having a comparable power conversion efficiency (PCE) to silicon solar cells. Overcoming drawbacks affecting their long-term stability is gaining incremental importance. Excess lead iodide (PbI ) causes perovskite degradation, although it aids in crystal growth and defect passivation.

Highly efficient p-i-n perovskite solar cells that endure temperature variations.

Daily temperature variations induce phase transitions and lattice strains in halide perovskites, challenging their stability in solar cells. We stabilized the perovskite black phase and improved solar cell performance using the ordered dipolar structure of β-poly(1,1-difluoroethylene) to control perovskite film crystallization and energy alignment. We demonstrated p-i-n perovskite solar cells with a record power conversion efficiency of 24.

Influence of Various Coal Energy Wastes and Foaming Agents on Foamed Geopolymer Materials' Synthesis.

The regularities of obtaining foamed alkali-activated geopolymer materials based on different wastes of coal power engineering (fly ash, fuel (boiler) slag, ash, and slag mixture) were considered. The phase composition of the studied waste showed the presence of a significant amount of the amorphous phase, as well as a crystalline phase. mostly in the form of high quartz.

Optical and Spin Properties of NV Center Ensembles in Diamond Nano-Pillars.

Nitrogen-vacancy (NV) color centers in diamond are excellent quantum sensors possessing high sensitivity and nano-scale spatial resolution. Their integration in photonic structures is often desired, since it leads to an increased photon emission and also allows the realization of solid-state quantum technology architectures. Here, we report the fabrication of diamond nano-pillars with diameters up to 1000 nm by electron beam lithography and inductively coupled plasma reactive ion etching in nitrogen-rich diamonds (type Ib) with [100] and [111] crystal orientations.