Direct liquid injection pulsed-pressure MOCVD of large area MoS on Si/SiO.

Large-scale, high-quality growth of transition metal dichalcogenides (TMD) of controlled thickness is paramount for many applications in opto- and microelectronics. This paper describes the direct growth of well-controlled large area molybdenum disulfide (MoS) on Si/SiO substrates by direct liquid injection pulsed-pressure metal-organic chemical vapor deposition (DLI-PP-MOCVD) using low-toxicity precursors. It is shown that control of the deposited thickness can be achieved by carefully tuning the amount of molybdenum precursor evaporated and that continuous layers are routinely obtained.

Determining by Raman spectroscopy the average thickness and -layer-specific surface coverages of MoS thin films with domains much smaller than the laser spot size.

Raman spectroscopy is a widely used technique to characterize nanomaterials because of its convenience, non-destructiveness, and sensitivity to materials change. The primary purpose of this work is to determine via Raman spectroscopy the average thickness of MoS thin films synthesized by direct liquid injection pulsed-pressure chemical vapor deposition (DLI-PP-CVD). Such samples are constituted of nanoflakes (with a lateral size of typically 50 nm, i.

Negative Magnetoresistivity in Highly Doped n-Type GaN.

This paper presents low-temperature measurements of magnetoresistivity in heavily doped n-type GaN grown by basic GaN growth technologies: molecular beam epitaxy, metal-organic vapor phase epitaxy, halide vapor phase epitaxy and ammonothermal. Additionally, GaN crystallized by High Nitrogen Pressure Solution method was also examined. It was found that all the samples under study exhibited negative magnetoresistivity at a low temperature (10 K < T < 50 K) and for some samples this effect was observed up to 100 K.