Carbon-coated Fe-Mn-O composites as promising anode materials for lithium-ion batteries.

Fe-Mn-O composite oxides with various Fe/Mn molar ratios were prepared by a simple coprecipitation method followed by calcining at 600 °C, and carbon-coated oxides were obtained by pyrolyzing pyrrole at 550 °C. The cycling and rate performance of the oxides as anode materials are greatly associated with the Fe/Mn molar ratio. The carbon-coated oxides with a molar ratio of 2:1 exhibit a stable reversible capacity of 651.

Enhanced electrochemical performance of FeWO4 by coating nitrogen-doped carbon.

FeWO4 (FWO) nanocrystals were prepared at 180 °C by a simple hydrothermal method, and carbon-coated FWO (FWO/C) was obtained at 550 °C using pyrrole as a carbon source. The FWO/C obtained from the product hydrothermally treated for 5 h exhibits reversible capacities of 771.6, 743.

Random composites of nickel networks supported by porous alumina toward double negative materials.

Random composites with nickel networks hosted randomly in porous alumina are proposed to realize double negative materials. The random composite for DNMs (RC-DNMs) can be prepared by typical processing of material, which makes it possible to explore new DNMs and potential applications, and to feasibly tune their electromagnetic parameters by controlling their composition and microstructure. Hopefully, various new RC-DNMs with improved performance will be proposed in the future.