Highly efficient NIR to NIR upconversion of ZnMoO:Tm,Yb phosphors and their application in biological imaging of deep tumors.

ZnMoO:Tm,Yb,K nano-phosphors with intense NIR to NIR (excitation by 980 nm, emission at ∼800 nm) upconversion were synthesized by a facile hydrothermal method. The nanoparticles were of the order of 200-400 nm. The XRD patterns confirmed a single phase triclinic structure despite doping small amounts of RE and alkali ions.

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads.

TiO2 immobilized on SiO2 (TiO2/SiO2) have been prepared by sol-gel method and various ions of transition metals (Cr3+, Co2+ Ni2+, CU2+, and Zn2+) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO2/SiO2 towards phenol degradation under black light irradiation were investigated and compared with undoped TiO2/SiO2. The results showed that the photoresponse of Cu2+ and Zn2+ doped TiO2/SiO2 were larger than undoped TiO2/SiO2, indicating that the photogenerated carriers were separated more efficiently in Cu2+ and Zn2+ doped TiO2/SiO2.

Chemical modification of carbonized wheat and barley straw using HNO3 and the adsorption of Cr(III).

The effects of oxidation using HNO(3) on the properties of the carbonized wheat and barley straw were investigated by measuring different properties such as specific surface area, PZC, total surface acidic groups as well as FTIR and TG-DTA. A small decrease in the specific surface area due to pore blockage was observed after oxidation. After oxidation, the acidity was increased considerably and the point of zero charge shifted from approximately pH 9 to pH 2 in both types of carbon.

Grape waste as a biosorbent for removing Cr(VI) from aqueous solution.

Grape waste generated in wine production is a cellulosic material rich in polyphenolic compounds which exhibits a high affinity for heavy metal ions. An adsorption gel was prepared from grape waste by cross-linking with concentrated sulfuric acid. It was characterized and utilized for the removal of Cr(VI) from synthetic aqueous solution.