Preparation and properties of plasma electrolytic oxidation coating on sandblasted pure titanium by a combination treatment.

Plasma electrolytic oxidation (PEO) is one of the most applicable methods to produce bioceramic coating on a dental implant and sandblasting is a primary technique to modify metal surface properties. This study aims to deposit bioceramic Ca- and P-containing coatings on sandblasted commercially pure titanium by PEO technique to improve its bioactive performance. The time-dependent modified surfaces are characterized in terms of their microstructure, phase, chemical composition, mechanical properties and bioactivities.

Ultrasonic enhancing amorphization during synthesis of calcium phosphate.

Amorphous calcium phosphate (ACP) has great application potential in biomaterials field due to its non-cytotoxicity, high bioactivity, good cytocompatibility, and so on. The results of this research demonstrated that ultrasonic obviously enhanced amorphization during synthesis of calcium phosphate. The ACP phase was relatively ideal when the solvent of Ca(NO3)2·4H2O was ethanol and the solvent of (NH4)2HPO4 was a mixture of water and ethanol, under ultrasonic.

Factors influencing the deposition of hydroxyapatite coating onto hollow glass microspheres.

Hydroxyapatite (HA) and HA coated microcarriers for cell culture and delivery have attracted more attention recently, owing to the rapid progress in the field of tissue engineering. In this research, a dense and uniform HA coating with the thickness of about 2 μm was successfully deposited on hollow glass microspheres (HGM) by biomimetic process. The influences of SBF concentration, immersion time, solid/liquid ratio and activation of HGM on the deposition rate and coating characteristics were discussed.

Effect of sintering on porosity, phase, and surface morphology of spray dried hydroxyapatite microspheres.

This article deals with the effect of sintering temperature on the physical and chemical characteristics of hydroxyapatite microspheres (HAMs) obtained by spray drying method. A set of specimens were sintered in a conventional furnace at 500-1100 degrees C. The surface morphology, phase composition, size distribution, specific surface area, and porosity were characterized by scanning electron microscope, X-ray diffractometer, laser diffraction particle size analyzer, and specific surface area analyzer, respectively.

Plasma-sprayed hydroxyapatite+titania composite bond coat for hydroxyapatite coating on titanium substrate.

A two-layer hydroxyapatite (HA)/HA+TiO(2) bond coat composite coating (HTH coating) on titanium was fabricated by plasma spraying. The HA+TiO(2) bond coat (HTBC) consists of 50 vol% HA and 50 vol% TiO(2) (HT). The microstructural characterization of the HTH coatings before and after heat treatment was conducted by using scanning electron microscopy (SEM), electron probe microanalyser (EPMA), X-ray diffractometer (XRD) and transmission electron microscopy (TEM), in comparison with that of HT coating and pure HA coating.

[The influence of the screw thread and the height of constraints on the stress distribution around dental implants by using three-dimensional finite element analysis].

Objective: To study the influence of the screw thread and the height of constraints on the stress distribution of the implants.

Methods: The three-dimensional emulational models of the implants with different screw-pitch were constructed by a CAD/CAM package. The Von Mises stress of the models was analyzed by three-dimensional finite element method.

[Investigation on the transition probability of the aluminum resonant double lines].

In order to obtain the aluminum resonant double lines, Al I 396.15 nm and Al I 394.40 nm, we have recorded the time-resolved spectra of the plasma induced by Nd:YAG laser ablating metal aluminum in Ar, under the Ar ambient pressure 10 kPa, at 0.