Resolidified Chalcogen-Assisted Growth of Bilayer Semiconductors with Controlled Stacking Orders.

Bilayer semiconductors have attracted much attention due to their stacking-order-dependent properties. However, as both 3R- and 2H-stacking are energetically stable at high temperatures, most of the high-temperature grown bilayer materials have random 3R- or 2H-stacking orders, leading to non-uniformity in optical and electrical properties. Here, a chemical vapor deposition method is developed to grow bilayer semiconductors with controlled stacking order by modulating the resolidified chalcogen precursors supply kinetics.

Growth of 2D Cr O -CrN Mosaic Heterostructures with Tunable Room-Temperature Ferromagnetism.

2D magnets have generated much attention due to their potential for spintronic devices. Heterostructures of 2D magnets are interesting platforms for exploring physical phenomena and applications. However, the controlled growth of 2D room-temperature ferromagnetic heterostructures is challenging.

Resolidified Chalcogen Precursors for High-Quality 2D Semiconductor Growth.

Two-dimensional (2D) semiconductors including transition metal dichalcogenides (TMDCs) have gained attention in optoelectronics for their extraordinary properties. However, the large amount and locally distributed lattice defects affect the optical properties of 2D TMDCs, and the defects originate from unstable factors in the synthesis process. In this work, we develop a method of pre-melting and resolidification of chalcogen precursors (sulfur and selenium), namely resolidified chalcogen, as precursor for the chemical vapor deposition growth of TMDCs with ultrahigh quality and uniformity.

Dual-metal precursors for the universal growth of non-layered 2D transition metal chalcogenides with ordered cation vacancies.

Two-dimensional (2D) transition metal chalcogenides (TMCs) are promising for nanoelectronics and energy applications. Among them, the emerging non-layered TMCs are unique due to their unsaturated dangling bonds on the surface and strong intralayer and interlayer bonding. However, the synthesis of non-layered 2D TMCs is challenging and this has made it difficult to study their structures and properties at thin thickness limit.

Layer-Dependent Raman Spectroscopy and Electronic Applications of Wide-Bandgap 2D Semiconductor β-ZrNCl.

In recent years, 2D layered semiconductors have received much attention for their potential in next-generation electronics and optoelectronics. Wide-bandgap 2D semiconductors are especially important in the blue and ultraviolet wavelength region, although there are very few 2D materials in this region. Here, monolayer β-type zirconium nitride chloride (β-ZrNCl) is isolated for the first time, which is an air-stable layered material with a bandgap of ≈3.