Methods: a comparative analysis of radiography, microcomputed tomography, and histology for bone tissue engineering.

This study focused on the assessment of radiography, microcomputed tomography, and histology for the evaluation of bone formation in a 15.0-mm defect in the rabbit radius after the implantation of a tissue-engineered construct. Radiography was found to be useful as a noninvasive method for obtaining images of calcified tissue throughout the time course of the experiment.

In vitro release of plasmid DNA from oligo(poly(ethylene glycol) fumarate) hydrogels.

This research investigates the release of plasmid DNA in vitro from novel, injectable hydrogels based on the polymer oligo(poly(ethylene glycol) fumarate) (OPF). These biodegradable hydrogels can be crosslinked under physiological conditions to physically entrap plasmid DNA. The DNA release kinetics were characterized fluorescently with the PicoGreen and OliGreen Reagents as well as through the use of radiolabeled plasmid.

In vivo degradation of porous poly(propylene fumarate)/poly(DL-lactic-co-glycolic acid) composite scaffolds.

This study investigated the in vivo degradation of poly(propylene fumarate) (PPF)/poly(DL-lactic-co-glycolic acid) (PLGA) composite scaffolds designed for controlled release of osteogenic factors. PPF/PLGA composites were implanted into 15.0mm segmental defects in the rabbit radius, harvested after 12 and 18 weeks, and analyzed using histological techniques to assess the extent of polymer degradation as well as the tissue response within the pores of the scaffolds.

Effect of varied release kinetics of the osteogenic thrombin peptide TP508 from biodegradable, polymeric scaffolds on bone formation in vivo.

This study was designed to assess the influence of varied release kinetics of the osteogenic thrombin peptide TP508 from osteoconductive poly(propylene fumarate)-based (PPF) composite scaffolds on bone formation in vivo. Four classes of scaffolds were constructed with different TP508 dosages (200, 100, or 0 microg) and release kinetics (large burst release, minimal burst release, or no release) and implanted in 15.0 mm segmental defects in rabbit radii.

Repair of rabbit segmental defects with the thrombin peptide, TP508.

The synthetic peptide, TP508 (Chrysalin), was delivered to rabbit segmental bone defects in biodegradable controlled-release PLGA microspheres to determine its potential efficacy for enhancing healing of non-critically and critically sized segmental defects. Non-critically sized radial defects were created in the forelimbs of New Zealand White rabbits, which were randomized into three treatment groups receiving 10, 50 and 100 microg doses of TP508 in the right radius and control microspheres (without TP508) in the left radius. Torsional testing of the radii at six weeks showed a significant increase in ultimate torque, failure torque, ultimate energy, failure energy, and stiffness when treated with TP508 compared to controls (p<0.

Controlled release of an osteogenic peptide from injectable biodegradable polymeric composites.

Poly(D,L-lactic-co-glycolic acid)/poly(ethylene glycol) (PLGA/PEG) blend microparticles loaded with the osteogenic peptide TP508 were added to a mixture of poly(propylene fumarate) (PPF), poly(propylene fumarate)-diacrylate (PPF-DA), and sodium chloride (NaCl) for the fabrication of PPF composite scaffolds that could allow for tissue ingrowth as well as for the controlled release of TP508 when implanted in an orthopedic defect site. In this study, PPF composites were fabricated and the in vitro release kinetics of TP508 were determined. TP508 loading within the PLGA/PEG microparticles, PEG content within the PLGA/PEG microparticles, the microparticle content of the PPF composite polymer component, and the leachable porogen initial mass percent of the PPF composites were varied according to a fractional factorial design and the effect of each variable on the release kinetics was determined for up to 28 days.