Saccharide-functionalized alkanethiols for fouling-resistant self-assembled monolayers: synthesis, monolayer properties, and antifouling behavior.

We describe the synthesis of a series of mono-, di-, and trisaccharide-functionalized alkanethiols as well as the formation of fouling-resistant self-assembled monolayers (SAMs) from these. The SAMs were characterized using ellipsometry, wetting measurements, and infrared reflection-absorption spectroscopy (IRAS). We show that the structure of the carbohydrate moiety affects the packing density and that this also alters the alkane chain organization.

Resistance of galactoside-terminated alkanethiol self-assembled monolayers to marine fouling organisms.

Self-assembled monolayers (SAMs) of galactoside-terminated alkanethiols have protein-resistance properties which can be tuned via the degree of methylation [Langmuir 2005, 21, 2971-2980]. Specifically, a partially methylated compound was more resistant to nonspecific protein adsorption than the hydroxylated or fully methylated counterparts. We investigate whether this also holds true for resistance to the attachment and adhesion of a range of marine species, in order to clarify to what extent resistance to protein adsorption correlates with the more complex adhesion of fouling organisms.

Fluorinated/siloxane copolymer blends for fouling release: chemical characterisation and biological evaluation with algae and barnacles.

Fouling-release coatings were prepared from blends of a fluorinated/siloxane copolymer with a poly(dimethyl siloxane) (PDMS) matrix in order to couple the low modulus character of PDMS with the low surface tension typical for fluorinated polymers. The content of the surface-active copolymer was varied in the blend over a broad range (0.15-10 wt % with respect to PDMS).

Poly(ethylene glycol)-containing hydrogel surfaces for antifouling applications in marine and freshwater environments.

This work describes the fabrication, characterization, and biological evaluation of a thin protein-resistant poly(ethylene glycol) (PEG)-based hydrogel coating for antifouling applications. The coating was fabricated by free-radical polymerization on silanized glass and silicon and on polystyrene-covered silicon and gold. The physicochemical properties of the coating were characterized by infrared spectroscopy, ellipsometry, and contact angle measurements.

Evaluation of a fully automated method to measure the critical removal stress of adult barnacles.

A computer-controlled force gauge designed to measure the adhesive strength of barnacles on test substrata is described. The instrument was evaluated with adult barnacles grown in situ on Silastic T2(R)-coated microscope slides and epoxy replicas adhered to the same substratum with synthetic adhesive. The force per unit area required to detach the barnacles (critical removal stress) using the new automated system was comparable to that obtained with ASTM D5618 (1994) (0.

Preparation and characterisation of silicone-based coatings filled with carbon nanotubes and natural sepiolite and their application as marine fouling-release coatings.

This article reports on the preparation and partial characterisation of silicone-based coatings filled with low levels of either synthetic multiwall carbon nanotubes (MWCNTs) or natural sepiolite (NS). The antifouling and fouling-release properties of these coatings were explored through laboratory assays involving representative soft-fouling (Ulva) and hard-fouling (Balanus) organisms. The bulk mechanical properties of the coatings appeared unchanged by the addition of low amounts of filler, in contrast to the surface properties, which were modified on exposure to water.