Fluorinated/siloxane copolymer blends for fouling release: chemical characterisation and biological evaluation with algae and barnacles.

Fouling-release coatings were prepared from blends of a fluorinated/siloxane copolymer with a poly(dimethyl siloxane) (PDMS) matrix in order to couple the low modulus character of PDMS with the low surface tension typical for fluorinated polymers. The content of the surface-active copolymer was varied in the blend over a broad range (0.15-10 wt % with respect to PDMS).

Evaluation of a fully automated method to measure the critical removal stress of adult barnacles.

A computer-controlled force gauge designed to measure the adhesive strength of barnacles on test substrata is described. The instrument was evaluated with adult barnacles grown in situ on Silastic T2(R)-coated microscope slides and epoxy replicas adhered to the same substratum with synthetic adhesive. The force per unit area required to detach the barnacles (critical removal stress) using the new automated system was comparable to that obtained with ASTM D5618 (1994) (0.

Preparation and characterisation of silicone-based coatings filled with carbon nanotubes and natural sepiolite and their application as marine fouling-release coatings.

This article reports on the preparation and partial characterisation of silicone-based coatings filled with low levels of either synthetic multiwall carbon nanotubes (MWCNTs) or natural sepiolite (NS). The antifouling and fouling-release properties of these coatings were explored through laboratory assays involving representative soft-fouling (Ulva) and hard-fouling (Balanus) organisms. The bulk mechanical properties of the coatings appeared unchanged by the addition of low amounts of filler, in contrast to the surface properties, which were modified on exposure to water.