Ultrasonic activation of adhesive systems increases bond strength and intratubular penetration of resin cement in root dentin subjected to radiation therapy.

Objective: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin.

Materials And Methods: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation.

Assessing push-out bond strength in re-irradiated teeth: Universal resin cement performance in self-etch and self-adhesive modes.

Objectives: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin.

Materials And Methods: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA).

Effect of the timing of radiation therapy on the push-out strength of resin cement to root dentine.

This study investigated the effect of radiation timing on the bond strength of resin cement to intraradicular dentine. Fifty human teeth were distributed into 5 groups (n = 10): Control (nonirradiated teeth), Before-RCT (teeth irradiated before root canal treatment), After-CH (teeth irradiated after canal preparation and placement of calcium hydroxide intracanal dressing), After-RCT (teeth irradiated after completion of root canal treatment) and After-FPL (teeth irradiated after luting of a glass fibre post). Each tooth received 70 Gy irradiation.

Effect of root perforation repair with mineral aggregate-based cements on the retention of customized fiberglass posts.

The purpose of this study was to investigate whether the root perforation repair with mineral aggregate-based cements affects the retention of customized fiberglass posts to bovine intraradicular dentin. Sixty-four bovine mandibular incisors had their root canals endodontically treated and prepared for fiberglass posts luting. Teeth were randomly distributed into four groups (n = 16), according to the cement used for the perforations repair (MTA HP; calcium aluminate cement-CAC; and CAC + calcium carbonate nanoparticles-nano-CaCO) and control group (no perforation).

Response of composite resins to preheating and the resulting strengthening of luted feldspar ceramic.

Objective: This study evaluated the influence of preheating different composite resins on their viscosity and strengthening yielded to ceramic.

Methods: Modulus of elasticity, Poisson's ratio, and degree of CC conversion were measured for three restorative composite resins (Z100-microhybrid; Empress Direct-nanohybrid; Estelite Omega-supranano) and one photoactivated resin cement (RelyX Veneer). Viscosity was measured during a heating-cooling curve (25°C-69°C-25°C) and also using isothermal analyses at 25°C and 69°C.

Nanofilled composite restorations with different adhesives strategies: clinical cases.

The esthetic procedures with composites are widely applied, both to posterior and anterior teeth to restore caries cavities, to replace failed restorations, or to make cosmetic procedures. The materials selected to each case may make the difference in the clinical result. This paper presents two clinical cases made with a nanofilled composite resin system used in different bond strategies.