Next generation highly resistant mirrors featuring all-silica layers.

A principal possibility to overcome fundamental (intrinsic) limit of pure optical materials laser light resistance is investigated by designing artificial materials with desired optical properties. We explore the suitability of high band-gap ultra-low refractive index material (n less than 1.38 at 550 nm) in the context of highly reflective coatings with enhanced optical resistance.

Femtosecond laser damage resistance of oxide and mixture oxide optical coatings.

We report on the laser damage resistance of ion beam-sputtered oxide materials (Al2O3, Nb2O5, HfO2, SiO2, Ta2O5, ZrO2) and mixtures of Al2O3-SiO2, Nb2O5-SiO2, HfO2-SiO2, Ta2O5-SiO2, and ZrO2-SiO2, irradiated by single 500 fs pulses at 1030 nm. Laser-induced damage threshold (LIDT), refractive index, and bandgaps of the single-layer coatings are measured. For pure oxide materials a linear evolution of the LIDT with bandgap is observed.

Characterization of zirconia- and niobia-silica mixture coatings produced by ion-beam sputtering.

ZrO2-SiO2 and Nb2O5-SiO2 mixture coatings as well as those of pure zirconia (ZrO2), niobia (Nb2O5), and silica (SiO2) deposited by ion-beam sputtering were investigated. Refractive-index dispersions, bandgaps, and volumetric fractions of materials in mixed coatings were analyzed from spectrophotometric data. Optical scattering, surface roughness, nanostructure, and optical resistance were also studied.