Investigation of Structural Phase, Mechanical, and Tribological Characteristics of Layer Gradient Heat-Protective Coatings Obtained by the Detonation Spraying Method.

This paper presents the results of a study of layer gradient thermal protection coatings based on NiCrAlY and YSZ obtained by detonation spraying. Modern gas turbines and high-temperature units operate under extreme temperatures and aggressive environments, which requires effective protection of components from wear, corrosion, and thermal shocks. In this study, the use of layer gradient coatings consisting of alternating layers of NiCrAlY and YSZ was investigated with the aim of solving the problem of thermal stress accumulation due to a smooth change in the composition of the layers.

A Study on Surface Hardening and Wear Resistance of AISI 52100 Steel by Ultrasonic Nanocrystal Surface Modification and Electrolytic Plasma Surface Modification Technologies.

In this study, a surface hardening of AISI 52100 bearing steel was performed by ultrasonic nanocrystal surface modification (UNSM), and electrolytic-plasma thermo-cyclic surface modification (EPSM), and their effects on the wear resistance were investigated. To evaluate the impact of these treatments on the wear resistance, the friction tests under dry conditions were conducted using a ball-on-disk tribometer in accordance with ASTM G99. The microstructure of the samples before and after treatment was characterized by scanning electron microscopy.

Effects of Electron Beam Irradiation on Mechanical and Tribological Properties of PEEK.

In this work, the mechanical and tribological characteristics of polyetheretherketone (PEEK) sheets were enhanced by electron beam irradiation. PEEK sheets irradiated at a speed of 0.8 m/min with a total dose of 200 kGy achieved the lowest specific wear rate of 4.

Effect of Bilayer Thickness and Bias Potential on the Structure and Properties of (TiZr/Nb)N Multilayer Coatings as a Result of Arc-PVD Deposition.

This work is devoted to the study of the formation of nanostructured multilayer coatings (TiZr/Nb)N on the surface of an AISI 321 steel substrate depending on the deposition parameters of the Arc-PVD method. The results of the X-ray diffraction analysis showed the formation of solid solution (TiNb)N and ZrN in the multilayer coatings with an FCC structure, ε-NbN with a hexagonal structure, as well as with a small volume fraction of the ε-TiN and β-NbN phase. On the basis of phase composition data, it is possible to assume that an increase in the number of bilayers leads to a decrease in the nitrogen concentration in the bilayers and, consequently, to a decrease in the volume fraction of ε-NbN and β-NbN nitrides.

Change of 0.34Cr-1Ni-Mo-Fe Steel Dislocation Structure in Plasma Electrolyte Hardening.

This work deals with the study of changes in the dislocation structure and quantitative characteristics, as well as morphological components, of 0.34Cr-1Ni-Mo-Fe steel before and after plasma electrolytic hardening. According to the electron microscopic studies of the fine structure of 0.