Effect of Oxalic Acid Treatment on Conductive Coatings Formed by Ni@Ag Core-Shell Nanoparticles.

Low-cost metallic nanoink based on nickel-silver core-shell nanoparticles (Ni@Ag NPs) was used for the formation of conductive metallic coatings with low sintering temperature, which can be successfully applied for replacement of currently used silver-based nanoinks in printed electronics. The effect of oxalic acid (OA) on the sintering temperature and conductivity of coatings formed by Ni@Ag NPs was evaluated. It was found that the addition of OA to the ink formulation and post-printing treatment of deposited films with this acid provided a noticeable decrease in the sintering temperature required for obtaining conductive patterns that is especially important for utilizing the polymeric substrates.

Polydispersity vs. Monodispersity. How the Properties of Ni-Ag Core-Shell Nanoparticles Affect the Conductivity of Ink Coatings.

The effect of polydispersity of nickel-silver core-shell nanoparticles (Ni-Ag NPs) on the conductivity of ink coatings was studied. Ni-Ag NPs of various average diameters (100, 220, and 420 nm) were synthesized and utilized for the preparation of conductive inks composed of monodisperse NPs and their polydisperse mixtures. The shell thickness of synthesized Ni-Ag NPs was found to be in the range of 10-20 nm and to provide stability of a core metal to oxidation for at least 6 months.

Application of metallic inks based on nickel-silver core-shell nanoparticles for fabrication of conductive films.

Conductive inks based on nickel nanoparticles (NPs) have attracted much attention as a low-cost replacement for the currently used silver and gold inks, for fabrication of printed electronic circuits and devices. Nickel NPs as a component of conductive inks should be stable against oxidation process at all stages of preparation of conductive patterns: ink formulation and storage, printing, and post-printing treatment. In the present study, the oxidation resistance of the Ag layer and the conductive properties of the Ni core allowed the use of nickel-silver core-shell (Ni@Ag) NPs as the component of conductive ink.