Electron Beam Welding of Dissimilar Stainless Steel and Maraging Steel Joints.

The incorporation of additive manufactured (AM) metal parts to real assemblies is a crucial issue for the increasing of their industrial utilization. The presented research is devoted to the electron beam welding (EBW) of dissimilar steel joints. Dissimilarity is defined by the various types of steel and manufacturing processes used for the creation of specimens.

Study of Eddy Current Testing Ability on SLM Aluminium Alloy.

The detection of defects in aluminium alloys using eddy current testing (ECT) can be restricted by higher electrical conductivity. Considering the occurrence of discontinuities during the selective laser melting (SLM) process, checking the ability of the ECT method for the mentioned purpose could bring simple and fast material identification. The research described here is focused on the application of three ECT probes with different frequency ranges (0.

Influence of AWJ Process Parameters on Erosion Groove Formation in Additively Manufactured Stainless Steel.

The presented manuscript focuses on the influence of process parameters of abrasive water jet technology on the creation of non-transient erosive grooves. The processed stainless steel SS 316L is additively manufactured using the selective laser melting (SLM) method. Due to the distinct mechanical properties of this material resulting from the production process, the material was machined in two planes according to the direction of the printing layers.

Residual Stress Evaluation in L-PBF-Produced SS 316L Specimens.

The identification of residual stresses (RS) in components made by selective laser melting (SLM) is necessary for subsequent technological optimization. The presented research is devoted to evaluating the influence of the combination of laser power (P), scanning velocity (v) and the rarely considered number of layers (n) on surface residual stresses in SLM stainless steel SS 316L. Experimental parameters were set based on the Design of Experiment (DoE) method, with follow-up X-ray diffraction (XRD) measurements and data processing using analysis of variance (ANOVA) and regression analysis.

Evaluation of the Depth and Width of Cuts after Controlled-Depth Abrasive Water Jet Machining Using Low Pressure.

The presented paper is focused on the evaluation of material removal during machining via an abrasive water jet with a controlled depth of cut. In the introductory parts of the work, a theoretical analysis of water jet technology and an analysis of the current state of the problem are presented. The experimental part of the work is devoted to testing the effects of technological parameters on material removal from the point of view of the maximum erosion depth and volume loss of material during machining with a low water pressure of 50 MPa.

Stress Relieving Heat Treatment of 316L Stainless Steel Made by Additive Manufacturing Process.

Residual stress occurs in the materials after different methods of processing due to the application of pressure and/or thermal gradient. The occurrence of residual stresses can be observed in both subtractive and additive-manufactured (AM) materials and objects. However, pressure residual stresses are considered, in some cases, to have a positive effect; there are applications where the neutral stress state is required.

Eddy Current Testing of Artificial Defects in 316L Stainless Steel Samples Made by Additive Manufacturing Technology.

Additive manufacturing has many positives, but its incorporation into functional parts production is restricted by the presence of defects. Eddy current testing provides solutions for their identification; however, some methodology and measurement standards for AM (additive manufacturing) products are still missing. The main purpose of the experiment described within this article was to check the ability of eddy current testing to identify AM stainless steel parts and to examine the data obtained by eddy currents variation under the influence of various types of designed artificial defects.