The Effect of HS Pressure on the Formation of Multiple Corrosion Products on 316L Stainless Steel Surface.

HS gas when exposed to metal can be responsible for both general and localized corrosion, which depend on several parameters such as HS concentration and the corrosion product layer formed. Therefore, the formation of passive film on 316L steel when exposed to HS environment was investigated using several analysis methods such as FESEM and STEM/EDS analyses, which identified a sulfur species underneath the porous structure of the passive film. X-ray photoelectron spectroscopy analysis demonstrated that the first layer of CrO and CrO was dissolved, accelerated by the presence of HS-Cl.