Interfacial surfactant competition and its impact on poly(ethylene oxide)/Au and poly(ethylene oxide)/Ag nanocomposite properties.

The structure and properties of nanocomposites of poly(ethylene oxide), with Ag and Au nanoparticles, surface modified with a 1:1 (by volume) oleylamine/oleic acid mixture, were investigated via transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, differential scanning calorimetry (DSC), infrared spectroscopy, dynamic mechanical analysis, and static mechanical testing. Results indicated that there was more oleylamine on Ag nanoparticles but more oleic acid on Au nanoparticles. This difference in surfactant populations on each nanoparticle led to different interfacial interactions with poly(ethylene oxide) and drastically influenced the glass transition temperature of these two nanocomposite systems.

Sulfated levan from Halomonas smyrnensis as a bioactive, heparin-mimetic glycan for cardiac tissue engineering applications.

Chemical derivatives of levan from Halomonas smyrnensis AAD6(T) with low, medium and high levels of sulfation were synthesized and characterized by FTIR and 2D-NMR. Sulfated levan samples were found to exhibit anticoagulation activity via the intrinsic pathway like heparin in a dose-dependent manner. Exceptionally high heparin equivalent activity of levan sulfate was shown to proceed via thrombin inhibition where decreased Factor Xa activity with increasing concentration was observed in antithrombin tests and above a certain concentration, levan sulfate showed a better inhibitor activity than heparin.

Rapid and efficient fabrication of multilevel structured silica micro-/nanofibers by centrifugal jet spinning.

A rapid and efficient method consisting of two simple steps, centrifugal jet spinning (CJS) and annealing, is introduced to fabricate multilevel structured silica micro-/nanofibers. Using this technique, which is 500 times faster than electrospinning, silica micro-/nanofibers with a hollow or porous internal structure are formed as a result of non-solvent evaporation induced phase separation in the spinning solution. Silica nanofibers with solid cross sections (364 nm and 781 nm), hollow cross sections (outer and internal diameters of 458 nm and 216 nm respectively), and encapsulated voids (outside diameter of 1.

Effect of surface modification on magnetization of iron oxide nanoparticle colloids.

Magnetic iron oxide nanoparticles have numerous applications in the biomedical field, some more mature, such as contrast agents in magnetic resonance imaging (MRI), and some emerging, such as heating agents in hyperthermia for cancer therapy. In all of these applications, the magnetic particles are coated with surfactants and polymers to enhance biocompatibility, prevent agglomeration, and add functionality. However, the coatings may interact with the surface atoms of the magnetic core and form a magnetically disordered layer, reducing the total amount of the magnetic phase, which is the key parameter in many applications.

NMR relaxation and pulsed-gradient diffusion study of polyethylene nanocomposites.

We performed pulsed-gradient spin-echo nuclear-magnetic-resonance (NMR) experiments on zinc oxide filled polyethylene. The molecular weights of the polyethylene samples ranged between 808 and 33,000 gmol, and four different zinc oxide samples were used: 27-, 33-, 51-, and 2500-nm-diameter particles. The results of these experiments showed that the diffusion coefficients of the polyethylene chains did not change with nanofiller content, but a drastic change is observed in the NMR relaxation spectrum in spin-spin-relaxation experiments.