Effect of thiourethane on the polymerization and mechanical properties of composite resin: A systematic review.

Statement Of Problem: Thiourethane has high chemical affinity with polymeric materials and its addition has been suggested for improving adhesives and composite resin. However, a systematic review of thiourethane addition is lacking.

Purpose: The purpose of this systematic review was to analyze the articles in the dental literature that studied the effect of thiourethane added to the resin matrix of dental materials related to polymerization shrinkage and mechanical properties.

Surface treatments of the zirconia-reinforced lithium disilicate ceramic in the adhesion to the resin cement.

This study verified the effect of surface treatments of the zirconia-reinforced lithium disilicate ceramic bonded to resin cement. Ceramic blocks were divided according to treatments (n=10): FA+SRX (Fluoric acid + silane RX), FA+MDP (Fluoric acid + MDP), FA+SCF+MDP (Fluoric acid + silane CF + MDP), FA+MEP (Fluoric acid + MEP), and MEP (Self-etch primer). Resin cement cylinders were made in the ceramic blocks, photoactivated with 1,200 mW/cm² for 40s, stored in water at 37°C for 24h, and evaluated by the microshear strength test, optical failure descriptive analysis (%), surface characterization (SEM) and contact angle (Goniometer).

Preheated acid associated with silane and electric current in the adhesion of the resin cement to ceramic.

This study verified the effect of the combination of preheated hydrofluoric acid/silane/electric current in the adhesion of the resin cement to ceramic. IPS E.max Press ceramic discs embedded in PVC rigid tubes were divided into four groups associating preheated hydrofluoric acid and silane applied with electrical current (n=10): Ha+S (Heated acid + silane); Ha+S+Ec (Heated acid + silane + electrical current); A+S (Acid + silane) and A+S+Ec (Acid + silano + electrical current).

Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling.

This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.

Dental displacement in complete dentures influenced by different flask types and polymerization cycles.

This study evaluated the dental displacement in dentures included in different flasks and processed by the Australian cycle modified or by microwave. Metal pins were placed on the teeth as reference for measurements: a) Incisal edge of maxillary and mandibular central incisors, buccal cusp of maxillary and mandibular vestibular first premolars, and mesiobuccal maxillary and mandibular cusps of second molars; b) Incisor to incisor, premolar to premolar and molar to molar; c) Left incisor to left molar and right incisor to right molar, and d) Vertical. Dentures were divided according to flasks (n=10): G1- Metal; G2- HH bimaxillary metal; G3-Microwaves; G4- HH bimaxillary microwaves.