Research on the integral forming process of thin walled and thick mouth seamless gas cylinders.

There is a considerable difference in wall thickness between the mouth and the cavity of thin-walled and thick-mouthed seamless gas cylinders, and the existing manufacturing processes are unable to effectively meet product requirements. To overcome such issue, a step-by-step boring-necking-spinning solution for gas cylinders was proposed, in which sufficient wall thickness is reserved for the mouth area of the cylinder blank, followed by necking-spinning to realize the overall forming of thin-walled, thick-mouthed seamless gas cylinders. The stress-strain distribution and geometric dimensional changes of gas cylinders during the spinning process were investigated by means of finite element simulation, and the effects of different process parameters on the stress and wall thickness of the bottle mouth were analyzed.

Study of the Microstructure and Corrosion Properties of a Ni-Based Alloy Coating Deposited onto the Surface of Ductile Cast Iron Using High-Speed Laser Cladding.

To improve the surface corrosion resistance of ductile iron, Ni-based alloy coatings were prepared using a high-speed laser cladding technology with different levels of laser power. The microstructure, phases, and corrosion properties of the coatings were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and an electrochemical workstation. Variations in laser power did not change the main phases of the coatings, which were composed of γ-Ni, NiB, NiSi, and CrC.

Microstructure and Wear Resistance of Laser Cladding of Fe-Based Alloy Coatings in Different Areas of Cladding Layer.

In this study, laser cladding technology was used to prepare Fe-based alloy coating on a 27SiMn hydraulic support, and a turning treatment was used to obtain samples of the upper and middle regions of the cladding layer. The influence of microstructure, phase composition, hardness, and wear resistance in different areas of the cladding layer was studied through scanning electron microscopy (SEM), X-ray diffractometry (XRD), friction and wear tests, and microhardness. The results show that the bcc phase content in the upper region of the cladding layer is less than that in the middle region of the cladding layer, and the upper region of the cladding layer contains more metal compounds.