Influence of TiN Inclusions and Segregation Bands on the Mechanical Properties and Delayed Crack in Thick NM550 Wear-Resistant Steel.

The formation mechanism of the delayed crack after flame cutting and mechanical properties in thick NM550 wear-resistant steel are studied by optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction, and an electron backscattered diffractometer. The delayed crack is formed at the segregation zone (SZ) located in the center of the 65 mm thick steel plate. The strength of the non-segregation zone (NSZ) with a martensite microstructure is slightly higher than that of SZ with a mixture microstructure of martensite plus bainite, and the plasticity of NSZ is significantly better than that of SZ.