Influence of Microstructure and Mechanical Properties of Dissimilar Rotary Friction Welded Inconel to Stainless Steel Joints.

The present study aims to evaluate the microstructure, grain size, and mechanical properties of the dissimilar AISI 316L/Inconel 718 (IN 718) rotary friction welded joints under both the as-welded and post-weld heat treatment (PWHT) conditions. Because of reduced flow strength at elevated temperatures, the AISI 316L and IN 718 dissimilar weldments exhibited more flash formation on the AISI 316L side. At higher rotating speeds during friction welding, an intermixing zone was created at the weld joint interface due to the material softening and squeezing.

Effect of Beam Oscillation on Microstructure and Mechanical Properties of Electron Beam Welded EN25 Steel.

EN25 steels have been found to be applicable in shafts, gears, etc., but welding of EN25 steel was performed using electron beam welding with different oscillation beam diameters varying from 2 mm to 0.5 mm.

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Rotary Friction Welded AA7075 and AA5083 Dissimilar Joint.

The present work aims to investigate the changes in the microstructural and mechanical properties of various pre- and post weld heat treatments (PWHTs) on rotary friction welded dissimilar (AA7075 and AA5083) aluminum alloys. The investigation focused on the evolution of weld macro- and microstructures, as well as the changes in hardness and tensile properties resulting from friction welding. The joint integrity was studied through various characterization techniques, and no cracks or incomplete bonding was observed.